Low haze polyethylene polymer compositions

ABSTRACT

Embodiments of a polyethylene polymer blend having a melt index (I 2 )&lt;2 g/10 min are provided, wherein the polyethylene polymer blend comprises at least about 50% by wt. of at least one high density polyethylene resin (HDPE) having a density ≧0.950 g/cm3, a melt index (I 2 )&lt;4 g/10 min; a melt flow ratio (I 10 /I 2 )≦9, and a molecular weight distribution (MWD) of about 2 to about 5; and further comprises about 1% to about 20% by wt. of at least one low density polyethylene resin (LDPE) having a density ≦0.930 g/cm3, a melt index (I 2 ) of about 0.1 to about 10 g/min, and an MWD&gt;3.

FIELD

Embodiments of the present disclosure are generally related to polyethylene polymer blends, and are specifically related to low haze polyethylene polymer blends comprising high density polyethylene (HDPE) and low density polyethylene (LDPE).

BACKGROUND

HDPE resins are used in various industrial applications and in various articles; however, these HDPE articles have optical properties which are unsuitable for clear flexible film applications. Accordingly, there may be a continual need for HDPE articles with improved optical properties.

SUMMARY

Embodiments of the present disclosure are directed to polyethylene polymer blends which demonstrate improved optical performance, such as reduced haze. According to one embodiment, a polyethylene polymer blend is provided. The polyethylene polymer blend comprises a melt index (I₂)<2 g/10 min, wherein I₂ is measured according to ASTM D1238 at 190° C. and 2.16 kg load, wherein the polyethylene polymer blend comprises at least about 50% by wt. of at least one high density polyethylene resin (HDPE) having a density ≧0.950 g/cm³, when measured according to ASTM D792, a melt index (I₂)<4 g/10 min, a melt flow ratio (I₁₀/I₂)≦9, where I₁₀ is measured according to ASTM D1238 at 190° C. and 10 kg load, and a molecular weight distribution (MWD) of about 2 to about 5, wherein MWD is defined as Mw/Mn with Mw being a weight average molecular weight and Mn being a number average molecular weight. The polyethylene polymer blend also comprises about 1% to about 20% by wt. of at least one low density polyethylene resin (LDPE) having a density ≦0.930 g/cm³, a melt index (I₂) of about 0.1 to about 10 g/min, and a MWD>3.

According to another embodiment, an article is produced from the above polyethylene polymer blends, wherein the article has a haze value ≦30% when measured according to ASTM-D-1003. In further embodiments, the article may be a blown monolayer film.

DETAILED DESCRIPTION

Embodiments of the present disclosure are directed to a polyethylene polymer blend having a melt index (I₂)<2 g/10 min, wherein I₂ is measured according to ASTM D1238 at 190° C. and 2.16 kg load.

The polyethylene polymer blend comprises at least about 50% by wt. of HDPE and at least about 1% to about 20% by wt. of LDPE. In further embodiments, the polyethylene polymer blend may comprise about 60% to about 98% by wt. HDPE, or about 70% to about 98% by wt. HDPE, or about 80% to about 98% by wt. HDPE, or about 90% to about 98% by wt. HDPE. Moreover, the polyethylene polymer blend may comprise about 1% to about 15% by wt. LDPE, or about 3% to about 15% by wt. LDPE, or about 3% to about 12% by wt. LDPE, or about 4% to about 10% by wt. LDPE.

Various density values are contemplated for the polyethylene polymer blend based on the amounts of the HDPE and LDPE used in the blend. In one more embodiments, the density of the polyethylene polymer blend is about 0.940 g/cm³, or at least about 0.950 g/cm³, or at least about 0.955 g/cm³. Moreover, the density may range from about 0.940 g/cm³ to 0.970 g/cm³, or about 0.950 g/cm³ to about 0.965 g/cm³, or about 0.950 g/cm³ to about 0.960 g/cm³. Density is measured in accordance with ASTM D 792.

The polyethylene polymer blend may have various properties which make it suitable for processing into a blown film. In one embodiment, the polyethylene polymer blend may have a molecular weight distribution (MWD) of about 2.5 to about 5, wherein MWD is defined as Mw/Mn with Mw being a weight average molecular weight and Mn being a number average molecular weight measured by GPC. In further embodiments, the MWD is from about or about 2 to about 4.5, or about 3 to about 5, or about 3.5 to about 4, or about 2.5 to about 4, or about 3 to about 4.

As stated above, the melt index (I₂) for the polyethylene polymer blend is less than 2 g/10 min. Moreover, in further embodiments, the melt index (I₂) of the polyethylene polymer blend is about 0.5 to about 1.5 g/10 min, or about 0.7 to about 1.2 g/10 min.

Further, the melt flow ratio (I₁₀/I₂) of the polyethylene polymer blend, where I₁₀ is measured according to ASTM D1238 at 190° C. and 10 kg load of the polyethylene polymer blend ≦9, or ≦8.5, or less than ≦8. Moreover, Moreover, the melt flow ratio (I₁₀/I₂) may range from about 6 to about 9, or about 6.5 to about 8.5, or about 7 to about 8.

High Density Polyethylene (HDPE)

The HDPE may have a density ≧0.950 g/cm³. In further embodiments, the density of the HDPE may be from about 0.955 to about 0.975 g/cm³, or about 0.955 to about 0.970 g/cm³, or about 0.955 to about 0.965 g/cm³, or about 0.960 to about 0.970 g/cm³

The HDPE may also have a melt index (I₂) less than 4 g/10 min, or less than 3 g/10 min, or less than 2 g/10 min. In additional embodiments, the melt index (I₂) of the HDPE is from about 0.1 to about 2.5 g/10 min, or from about 0.1 to 2.0 g/10 min, or about 0.5 to about 2 g/10 min, or about 0.2 to about 1.5 mg/10 min, or about 0.5 to about 1.5 g/10 min.

The HDPE may have a melt flow ratio (I₁₀/I₂)≦9, where I₁₀ is measured according to ASTM D1238 at 190° C. and 10 kg load polymer blend, or ≦8.5, or less than ≦8. Moreover, the melt flow ratio (I₁₀/I₂) may range from about 6 to about 9, or about 6 to about 8.5, or about 6 about 8, or about 7 to about 8.

Further, the HDPE may have a molecular weight distribution (MWD) about 2 to about 5, or about 2.5 to about 4.5, or about 3 to about 5, or about 3.5 to about 4, or about 2.5 to about 4, or about 3 to about 4.

These HDPE polymers may be produced via various processes familiar to one of ordinary skill in the art, for example, Ziegler-Natta catalyzed polymerization processes. Moreover, it is suitable to produce the present HDPE examples in a single reactor or multiple reactors. While HDPE Examples 1-3 in the tables below are produced in a single reactor, it is contemplated to use multiple reactors for various reasons e.g., reducing the time required to achieve the HDPE resin.

Low Density Polyethylene (LDPE)

The LDPE may have a density ≦0.930 g/cm³, or about 0.915 to 0.930 g/cm³. The LDPE may have a melt index (I₂) less than 10 g/10 min, or less than 5 g/10 min, or less than 2 g/10 min. Stated differently, the LDPE may have a melt index (I₂) of about 0.1 to about 10 g/min, or about 0.5 to about 10 g/10 min, or about 0.5 to about 8 g/10 min, or about 1 to about 8 g/10 min, or about 2 to about 7 g/10 min. The LDPE may have an MWD value of at least 3, or about 3.5 to about 10, or about 4 to about 10, or about 5 to about 9.

Various compositional embodiments are suitable as LDPEs. Such LDPEs may be commercially available under the tradenames AGILITY™ (e.g., AGILITY 1000, AGILITY 1001, and AGILITY 1021), DOW™ LDPE 6401, DOW™ LDPE 6211, and DOW™ LDPE 7511, all of which are available from The Dow Chemical Company (Midland, Mich.)

Additional optional materials may be added to the polyethylene polymer blend of the present disclosure. For example, these materials may include nucleating agents, antioxidants, antibacterial agents, ultraviolet absorbers, light stabilizers, neutralizers, antistatic agents, antiblocking agents, flame retardants, lubricants, various other processing aids and fillers, and the like and mixtures thereof. In embodiments including nucleating agents, the polyethylene polymer blend may comprise about 100 to about 2000 ppm of nucleating agent, or about 500 to about 1000 ppm of nucleating agent.

The polyethylene polymer blends may be utilized in the fabrication of various articles. For example and not by way of limitation, the article may be a blown monolayer film. Various thicknesses are contemplated for the blown monolayer film. For example, the blown monolayer film may have a thickness of about 0.1 mil to about 5 mils, or about 0.5 mils to about 2 mils, or about 0.5 to about 1.5 mils, or about 0.8 to about 1.2 mils.

The articles of the present disclosure, which may be a blown monolayer film or another suitable structure, demonstrate suitable optical properties. For example, the article may demonstrate a total haze ≦30%, or a total haze value ≦25%, or a or a total haze value ≦20%, or a total haze value ≦15%, or a total haze value ≦10% when measured according to ASTM-D-1003. In a specific embodiment, a blown monolayer film having a thickness of about 0.5 to about 1.5 mils demonstrates a haze value ≦25%, or a haze value ≦20%.

In addition to optical results, the strength of the blown monolayer film or article may be characterized one or more of the following metrics. One such metric is secant modulus. In specific embodiments, the article may have a 2% secant modulus greater than 90,000 psi in the machine direction in accordance with ASTM D882-12, or a 2% secant modulus greater than 100,000 psi. Additionally, lower tear strength may be also be desired for the present articles, specifically in plastic wrap materials. In one embodiment, the article may have a tear strength of less than 35 g in the machine direction in accordance with ASTM D882-12, or less than 30 g in the machine direction.

Testing Methods

Density

Samples for density measurement are prepared according to ASTM D1928. Measurements are made using ASTM D792, Method B.

Melt Index

Melt index, or I₂, is determined according to ASTM D1238 at 190° C., 216 kg. Melt index, or I₁₀, is measured in accordance with ASTM D1238 at 190° C., 10 kg.

GPC Method

The gel permeation chromatographic system consists of either a Polymer Laboratories Model PL-210 or a Polymer Laboratories Model PL-220 instrument. The column and carousel compartments are operated at 140° C. Three Polymer Laboratories 10-micron Mixed-B columns are used. The solvent is 1,2,4-trichlorobenzene. The samples are prepared at a concentration of 0.1 grams of polymer in 50 milliliters of solvent containing 200 ppm of butylated hydroxytoluene (BHT). Samples are prepared by agitating lightly for 2 hours at 160° C. The injection volume used is 100 microliters and the flow rate is 1.0 ml/minute.

Calibration of the GPC column set is performed with 21 narrow molecular weight distribution polystyrene standards with molecular weights ranging from 580 to 8,400,000, arranged in 6 “cocktail” mixtures with at least a decade of separation between individual molecular weights. The standards are purchased from Polymer Laboratories (Shropshire, UK). The polystyrene standards are prepared at 0.025 grams in 50 milliliters of solvent for molecular weights equal to or greater than 1,000,000, and 0.05 grams in 50 milliliters of solvent for molecular weights less than 1,000,000. The polystyrene standards are dissolved at 80° C. with gentle agitation for 30 minutes. The narrow standards mixtures are run first and in order of decreasing highest molecular weight component to minimize degradation. The polystyrene standard peak molecular weights are converted to polyethylene molecular weights using the following equation (as described in Williams and Ward, J. Polym. Sci., Polym. Let., 6, 621 (1968)): M_(polyethylene)=0.4316×(M_(polystyrene)). Polyethylene equivalent molecular weight calculations are performed using Viscotek TriSEC software Version 3.0.

Number- and weight-average molecular weights were calculated according to the following equations:

$M_{n} = \frac{\sum\limits^{i}{Wf}_{i}}{\sum\limits^{i}\left( {{Wf}_{i}/M_{i}} \right)}$ $M_{w} = \frac{\sum\limits^{i}\left( {{Wf}_{i}*M_{i}} \right)}{\sum\limits^{i}{Wf}_{i}}$

wherein Mn is the number average molecular weight, Mw, is the weight average molecular weight, and Wf_(i) is the weight fraction of the molecules with a molecular weight of M_(i).

Tensile Properties

Tensile break stress, tensile break strain, and 2% secant modulus are measured in the machine direction (MD) and cross direction (CD) with an Instron universal tester according to ASTM D882-12. Five specimens for each material are tested and average numbers are reported.

Optical Properties

Film gloss at 45° is determined using ASTM D2457. Total haze of the films is measured according to ASTM D1003. Clarity of the films is done according to ASTM D1746.

EXAMPLES

The following discusses the production of exemplary polyethylene polymer blend and methods of making these polyethylene polymer blends. Additionally, the following discussion discloses methods of producing films from the polyethylene polymer blends. In addition to the procedures, the properties of the polyethylene polymer blends and films produced therefrom are also provided below.

Resin Fabrication

The polyethylene resins are produced via a solution polymerization according to the following exemplary process. All raw materials (monomer and comonomer) and the process solvent (a narrow boiling range high-purity isoparaffinic solvent trademarked Isopar E and commercially available from Exxon Mobil Corporation) are purified with molecular sieves before introduction into the reaction environment. Hydrogen is supplied in pressurized cylinders as a high purity grade and is not further purified. The reactor monomer feed stream is pressurized via a mechanical compressor to above reaction pressure. The solvent and comonomer feed is pressurized via a mechanical positive displacement pump to above reaction pressure. The individual catalyst components are manually batch diluted to specified component concentrations with purified solvent (Isopar E) and pressured to above reaction pressure. All reaction feed flows are measured with mass flow meters and independently controlled with computer automated valve control systems.

The fresh comonomer feed is mechanically pressurized and can be injected into the process at several potential locations depending on reactor configuration which include: only the feed stream for the first reactor, only the feed stream for the second reactor, both the first and second reactor feed streams independently, or into a common stream prior to the solvent split to the two reactors. Some comonomer injection combinations are only possible when running dual reactor configuration.

Reactor configuration options include single reactor operation, dual series reactor operation, or dual parallel reactor operation.

The continuous solution polymerization reactor consists of a liquid full, non-adiabatic, isothermal, circulating, loop reactor. Independent control of all fresh solvent, monomer, comonomer, hydrogen, and catalyst component feeds is possible. The total fresh feed stream to the reactor (solvent, monomer, comonomer, and hydrogen) is temperature controlled by passing the feed stream through a heat exchanger. The total fresh feed to the polymerization reactor is injected into the reactor at two locations with approximately equal reactor volumes between each injection location. The fresh feed is controlled with each injector receiving half of the total fresh feed mass flow. The catalyst components are injected into the polymerization reactor through a specially designed injection stinger and are combined into one mixed catalyst/cocatalyst feed stream prior to injection into the reactor. The primary catalyst component feed is computer controlled to maintain the reactor monomer concentration at a specified target. The cocatalyst component(s) is/are fed based on calculated specified molar ratios to the primary catalyst component. Immediately following each fresh injection location (either feed or catalyst), the feed streams are mixed with the circulating polymerization reactor contents with static mixing elements. The contents of the reactor are continuously circulated through heat exchangers responsible for removing much of the heat of reaction and with the temperature of the coolant side responsible for maintaining an isothermal reaction environment at the specified temperature. Circulation around the reactor loop is provided by a positive displacement pump.

In dual series reactor configuration the effluent from the first polymerization reactor (containing solvent, monomer, comonomer, hydrogen, catalyst components, and molten polymer) exits the first reactor loop and is added to the second reactor loop downstream of the second reactor lower pressure fresh feed injection.

In dual parallel reactor configuration the effluent streams from the first and the second polymerization reactors are combined prior to any additional processing.

In all reactor configurations the final reactor effluent (second reactor effluent for dual series, the combined effluent for dual parallel, or the single reactor effluent) enters a zone where it is deactivated with the addition of and reaction with water. At this same reactor exit location other additives may also be added (such as an acid scavenging agent and anti-oxidants. The stream then goes through a static mixer to disperse the post reactor additive components.

Following catalyst deactivation and additive addition, the reactor effluent passes through a heat exchanger to raise the stream temperature in preparation for separation of the polymer from the other lower boiling reaction components. The stream then passes through a pressure let down control valve (responsible for maintaining the pressure of the reactor at a specified target). The stream then enters a two stage separation and devolatization system where the polymer is removed from the solvent, hydrogen, and unreacted monomer and comonomer. The recycled stream is purified before entering the reactor again. The separated and devolatilized polymer melt is pumped through a die specially designed for underwater pelletization, cut into uniform solid pellets, dried, and transferred into a hopper. After validation of initial polymer properties, the solid polymer pellets are manually dumped into a box for storage. Each box typically holds 1200 pounds of polymer pellets.

The non-polymer portions removed in the devolatilization step pass through various pieces of equipment which separate most of the ethylene which is removed from the system to a vent destruction unit. Most of the solvent and unreacted comonomer is recycled back to the reactor after passing through molecular sieve purification beds, a small amount of solvent is purged from the process as co-product.

TABLE 1 Processing Parameters for Exemplary HDPE Polymers Units Example 1 Example 2 Example 3 1. REACTOR FEEDS Reactor Feed deg C. 54 55 54 Temperature Reactor Total Solvent lbs/h 1481 1457 1739 Flow Reactor Fresh Ethylene lbs/h 385 378 422 Flow Reactor Total Ethylene lbs/h 396 389 436 Flow Comonomer Type Used None None None Reactor Fresh lbs/h 0.0 0.0 0.0 Comonomer Flow Reactor Total lbs/h 0.0 0.0 0.0 Comonomer Flow Reactor % 0.0 0.0 0.0 Comonomer/Olefin Ratio Reactor Feed Ratio 3.84 3.85 4.12 Solvent/Ethylene Ratio Reactor Fresh Hydrogen sccm 4551 2874 7914 Flow Reactor Hydrogen Mole mol % 0.18 0.11 0.30 Percent 2. REACTION Reactor Configuration Single reactor Single reactor Single reactor Reactor Control deg C. 195 208 185 Temperature Reactor Pressure psig 725 725 725 Reactor Ethylene % 92.9 92.8 92.3 Conversion Reactor FTnIR Exit C2 g/L 9.0 9.0 9.4 Concentration Reactor Viscosity centi- 1447 1147 1225 Poise Reactor Polymer hrs 0.11 0.10 0.09 Residence Time 3. CATALYST Reactor Catalyst Type ZN-CAT ZN-CAT ZN-CAT Reactor Catalyst 10⁶ lbs 0.72 0.53 0.68 Efficiency polymer/ lb Ti Reactor Co-Catalyst Ratio 4.0 4.0 4.0 Molar Ratio Reactor Co-Catalyst triethylaluminum triethylaluminum triethylaluminum Type (TEA) (TEA) (TEA)

TABLE 2 Processing Parameters for Comparative HDPE Polymers Comp. Comp. Comp. Comp. Comp. Comp. Units Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 1. REACTOR FEEDS Primary Reactor ° C. 40 40 40 40 60 60 Feed Temperature Primary Reactor lbs/h 1266 1346 1424 979 1143 1746 Total Solvent Flow Primary Reactor lbs/h 221 236 251 208 154 238 Fresh Ethylene Flow Primary Reactor lbs/h 231 248 262 216 163 251 Total Ethylene Flow Comonomer Type 1-Octene None None None None None Used Primary Reactor lbs/h 0.98 0.00 0.00 0.00 0.00 0.00 Fresh Comonomer Flow Primary Reactor lbs/h 1.95 0.00 0.00 0.00 0.00 0.00 Total Comonomer Flow Primary Reactor Ratio 5.73 5.68 5.68 4.71 7.42 7.33 Feed Solvent/Ethylene Ratio Primary Reactor sccm 4185 4965 4691 7325 691 2500 Fresh Hydrogen Flow Primary Reactor mol % 0.28 0.31 0.27 0.52 0.06 0.15 Hydrogen Mole Percent Secondary ° C. 40 40 40 40 40 39 Reactor Feed Temperature Secondary lbs/h 526 560 592 604 700 486 Reactor Total Solvent Flow Secondary lbs/h 199 212 225 226 263 184 Reactor Fresh Ethylene Flow Secondary lbs/h 203 216 229 232 269 187 Reactor Total Ethylene Flow Secondary lbs/h 0.0 0.0 0.0 0.0 0.0 0.0 Reactor Fresh Comonomer Flow Secondary lbs/h 0.40 0.0 0.0 0.0 0.0 0.0 Reactor Total Comonomer Flow Secondary Ratio 2.64 2.65 2.63 2.66 2.65 2.65 Reactor Feed Solvent/Ethylene Ratio Secondary sccm 16603 19122 16985 100 36643 49678 Reactor Fresh Hydrogen Flow Secondary mol % 1.25 1.34 1.12 0.007 2.05 3.90 Reactor Hydrogen Mole Percent Overall Ratio 0.53 0.0 0.0 0.0 0.0 0.0 Comonomer/Olefin Ratio 2. REACTION Reactor Dual Dual Dual Dual Dual Dual Configuration Series Series Series Series Series Series Primary Reactor ° C. 170 170 170 160 159 160 Control Temperature Primary Reactor psig 725 725 725 725 725 725 Pressure Primary Reactor % 80.3 80.4 80.5 85.1 74.5 74.5 Ethylene Conversion Primary Reactor g/L 18.5 18.4 18.4 16.7 19.6 19.4 FTnIR Exit Ethylene Concentration Primary Reactor centiPoise 1710 1288 830 477 3560 960 Viscosity Primary Reactor hrs 0.23 0.21 0.20 0.29 0.26 0.17 Polymer Residence Time Secondary ° C. 195 195 195 190 195 195 Reactor Control Temperature Secondary psig 726 727 726 729 730 724 Reactor Pressure Secondary % 87.2 87.0 87.0 82.1 90.0 86.1 Reactor Ethylene Conversion Secondary g/L 8.6 8.7 8.7 14.0 8.2 7.8 Reactor FTnIR Exit Ethylene Concentration Secondary centiPoise 422 334 248 822 359 168 Reactor Viscosity Secondary hrs 0.09 0.08 0.08 0.10 0.09 0.07 Reactor Polymer Residence Time Overall Ethylene % 92.9 92.6 92.5 89.6 92.8 92.0 Conversion by vent 3. CATALYST Primary Reactor m-CAT m-CAT m-CAT m-CAT m-CAT m-CAT Catalyst Type Primary Reactor 10⁶ lbs 3.77 3.17 2.88 2.99 1.94 1.93 Catalyst Efficiency polymer/ lb Zr Primary Reactor Ratio 2.48 2.54 2.33 2.49 2.50 2.48 Co-Catalyst-1 Molar Ratio Primary Reactor RIBS-2 RIBS-2 RIBS-2 RIBS-2 RIBS-2 RIBS-2 Co-Catalyst-1 Type Primary Reactor Ratio 10.0 10.0 10.0 10.0 10.0 10.0 Co-Catalyst-2 Molar Ratio Primary Reactor MMAO- MMAO- MMAO- MMAO- MMAO- MMAO- Co-Catalyst-2 3A 3A 3A 3A 3A 3A Type Secondary m-CAT m-CAT m-CAT m-CAT m-CAT m-CAT Reactor Catalyst Type Secondary 10⁶ lbs 0.88 1.14 1.14 2.37 0.99 0.94 Reactor Catalyst polymer/ Efficiency lb Zr Secondary Ratio 1.5 1.5 1.5 1.5 1.5 1.5 Reactor Co- Catalyst-1 Molar Ratio Secondary RIBS-2 RIBS-2 RIBS-2 RIBS-2 RIBS-2 RIBS-2 Reactor Co- Catalyst-1 Type Secondary Ratio 3.0 3.0 3.0 3.0 3.0 3.0 Reactor Co- Catalyst-2 Molar Ratio Secondary MMAO- MMAO- MMAO- MMAO- MMAO- MMAO- Reactor Co- 3A 3A 3A 3A 3A 3A Catalyst-2 Type

TABLE 3 Catalyst from Tables 1 and 2 (CAS name) m-CAT Zirconium, [2,2′″-[I,3-pro- panediylbis(oxy- 

 O)]bis[3″,5,5″-tris(1,1- dimethylethyl)-5′-methyl[1,1′:3′,1″-terphe- nyl]-2′-olato- 

 O]]dimethyl-, (OC-6-33)- RIBS-2 Amines, bis(hydrogenated tallow alkyl)methyl, tetrakis(pentafluorophenyl)borate(1-) MMAO-3A Aluminoxanes, iso-Bu Me, branched, cyclic and linear; modified methyl 3A aluminoxane

The ZN-CAT was prepared according to the following procedure. Ethylaluminium dichloride (EADC) solution (15 wt % EADC dissolved in Isopar E) was transferred into the stirred vessel containing magnesium chloride (MgCl₂) slurry (0.2M in Isopar E) and let to age while stirring for 6 hours prior to use. Titanium tetraisopropoxide (Ti(OiPr)₄) was transferred to the MgCl₂/EADC slurry vessel, followed by at least 8 hours of aging to obtain the procatalyst. The ratio of MgCl₂:EADC:Ti(OiPr)₄ was such that the metal ratio (Mg:Al:Ti) in the procatalyst 1 was 40:12.5:3.

TABLE 4 Properties of HDPE Resins and HDPE/LDPE melt blend I₂ Density Composition (g/min) I₁₀/I₂ Mw/Mn (g/cc) Note Comp. Ex. 1 0.91 11 4.8 0.955 Dual reactor Comp. Ex. 2 1.2 10.2 4.0 0.9601 Dual reactor Comp. Ex. 3 1.89 9.6 3.6 0.9603 Dual reactor Comp. Ex. 4 0.83 8.9 2.0 0.9543 Dual reactor Comp. Ex. 5 0.76 31.9 11.3 0.9708 Dual reactor Comp. Ex. 6 0.8 12.4 20.0 0.9679 Dual reactor ELITE 5960G 0.85 11.0 5.1 0.9615 Dual reactor Ex. 1 1.0 7.5 3.6 0.9591 Single reactor Ex. 2 1.0 7.7 4.0 0.9593 Single reactor Ex. 3 1.0 7.0 3.6 0.9587 Single reactor 97 wt % Example 3/ 1.0 7.0 3.6 0.9579 Blend 3% AGILITY 1021 melt blend

TABLE 5 Properties of the LDPE resins I₂ Density Mw/Mn (g/10 min) (g/cc) DOW LDPE 640I 4.8 2 0.9200 DOW AGILITY 6.4 1.85 0.9195 1021 LDPE 621I 9.3 2.3 0.9180 DOW AGILITY 7.5 0.19 0.9195 1000 DOW AGILITY 6.1 0.65 0.9200 1001 DOW LDPE 7.2 6.4 0.9250 751A1

Film Fabrication

As shown in Tables 6-8 below, 1-mil monolayer films were fabricated from the HDPE resins and the LDPE resins above using a blown film line. The HDPE and LDPE were dry blended in the amounts listed below. The dry blend was dropped in to the hopper of the extruder for making the blown film. The blown film line was equipped with an annular die with a diameter of 8 inch and a die gap of 70 mils. Blow up ratio (BUR) is 2.5:1 and frost line height (FLH) is 40 inch. Output rate is 260 lbs/h. The melt temperature is 440° F.

In addition to the dry blended films of Tables 6-8 below, Tables 4 and 6 also list a melt blend produced from 97% by wt of Example 3 HDPE and 3% by wt. AGILITY 1021 LDPE. This process was performed on the Farrel CP 250 continuous mixer; with a horsepower rating of 40 hp on the extruder and 60 hp on the mixer. The mixer was equipped with the 2.88 inch, 7/15 rotor combination with two dams at the 5 and 6 positions and no vent. Nitrogen was fed to the mixer feed throat at 5 SCFH. Material was melted and compounded in the mixer. The residence time was controlled by a feed rate of 200 pounds per hour, orifice opening of 50%, and mixer screw speed of 450 RPM. Maximum RPM of the mixer is 850. Once mixed, the compounded ribbon was then fed into the 4 inch 11/1 L/D single screw extruder to be extruded into strands at 28 RPM. Maximum RPM of the extruder is 100. The pusher was not used. An eight-hole strand die with 4.0 mm diameter holes was utilized. The strands were run through about half of a 16 foot water bath as a single pass, then passed through a Berlyn Air Knife to remove excess water. Then the strands were chopped into pellets via a Scheer pelletizer. The chopped pellets were passed over a classifier which culled out fines and longs and then discharged into a 15 gallon plastic drum. The pellets were transferred to a hopper via a vacuum loading system then dropped into lined cartons. The cartons were purged at least two days with nitrogen.

TABLE 6 Properties of the films 2% 2% Secant Secant Modulus, Modulus, Clarity Gloss Haze CD MD Tear, CD Tear, MD Unit % % % psi psi gram Gram ELITE 5960G 75 11 54 129,159 110,736  351 12 90 wt % ELITE 85 17 39 116,455 98,323 676 13 5960G/10 wt % AGILITY 1021 90 wt % Comp. Ex. 1/ 95 20 34 119,704 95,946 1092 11 10 wt % AGILITY 1021 90 wt % Comp. Ex. 2/ 93 18 41 136,361 108,796 791 12 10 wt % AGILITY 1021 90 wt % Comp. Ex. 3/ 87 13 52 136,606 105,365 278 12 10 wt % AGILITY 1021 Comp. Ex. 4 24 7 83 109,721 95,699 214 24 90 wt % Comp. Ex. 4/ 96 25 35 118,235 92,983 351 17 10 wt % AGILITY 1021 Comp. Ex. 5 57 6 79 103,983 104,844 372 15 90 wt % Comp. Ex. 1/ 82 13 46 100,977 92,578 161 12 10 wt % AGILITY 1021 Ex. 1 92 20 35 153,903 109,298 251 21 90 wt % Ex. 1/10 wt % 98 44 17 127,945 103,259 396 14 AGILITY 1021 Tensile Tensile Break Tensile Yield Tensile Tensile Tensile Stress, Break Stress, Break Break Yield CD Strain, CD CD Stress, MD Strain, MD Stress, MD Unit psi % psi psi % Psi ELITE 5960G 3,086 384 3,856 4,924 532 3,625 90 wt % ELITE 2,680 556 4,162 4,372 517 3,307 5960G/10 wt % AGILITY 1021 90 wt % Comp. Ex. 1/ 2,362 354 3,567 2,641 531 3,829 10 wt % AGILITY 1021 90 wt % Comp. Ex. 2/ 2,582 369 3,853 4,795 523 3,908 10 wt % AGILITY 1021 90 wt % Comp. Ex. 3/ 2,389 355 3,628 2,077 390 3,792 10 wt % AGILITY 1021 Comp. Ex. 4 4,946 788 3,791 6,049 635 3,651 90 wt % Comp. Ex. 4/ 3,094 467 4,026 5,812 661 3,620 10 wt % AGILITY 1021 Comp. Ex. 5 1,027 63 1,657 1,462 249 1,557 90 wt % Comp. Ex. 1/ 1,066 3 1,066 1,246 248 1,598 10 wt % AGILITY 1021 Ex. 1 3,929 656 4,292 5,309 556 3,909 90 wt % Ex. 1/10 wt % 3,069 515 3,939 5,064 592 3,628 AGILITY 1021

The following tables depict the effect of increasing LDPE amounts for the present exemplary polyethylene polymer blends.

TABLE 7 Ex. 1 HDPE polyethylene polymer blends 2% 2% Secant Secant Modulus, Modulus, Clarity Gloss Haze CD MD Tear, CD Tear, MD Unit % % % psi psi Gram Gram 90 wt % Ex. 1/10 wt % 98 45 18 133,662 107,281 427 18 AGILITY 1021 98 wt % Ex. 1/2 wt % 96 28 28 151,620 122,729 211 21 AGILITY 1021 96 wt % Ex. 1/4 wt % 96 33 26 137,786 114,585 261 20 AGILITY 1021 94 % wt Ex. 1/6 wt % 97 33 24 145,766 119,691 341 18 AGILITY 1021 97 wt % Ex. 3/3 wt % 97 36 23 120,343 103,027 266 21 AGILITY 1021 melt blend Tensile Break Tensile Tensile Tensile Tensile Tensile Stress, Break Yield Break Break Yield CD Strain, CD Stress, CD Stress, MD Strain, MD Stress, MD Unit psi % psi Ppsi % Psi 90 wt % Ex. 1/10 wt % 3,493 541 4,046 4,932 562 3,774 AGILITY 1021 98 wt % Ex. 1/2 wt % 4,640 736 4,343 5,499 616 3,864 AGILITY 1021 96 wt % Ex. 1/4 wt % 4,577 727 4,254 5,774 646 3,863 AGILITY 1021 94 % wt Ex. 1/6 wt % 4,549 705 4,246 5,328 624 3,778 AGILITY 1021 97 wt % Ex. 3/3 wt % 4,163 687 3,907 4,472 580 3,769 AGILITY 1021 melt blend

TABLE 8 Ex. 2 HDPE polyethylene polymer blends 2% 2% Secant Secant Modulus, Modulus, Tear, Tear, Clarity Gloss Haze CD MD CD MD Unit % % % psi psi gram gram Ex. 2 95 28 27 154,162 128,855 258 23 97 wt % Ex. 2/3 wt % LDPE 640I 96 32 25  29,625 114,631 287 21 90 wt % Ex. 2/10 wt % LDPE 640I 98 40 20 128,362 104,178 355 18 97 wt % Ex. 2/3 wt % AGILITY 1021 96 32 25 142,800 106,760 350 18 90 wt % Ex. 2/10 wt % AGILITY 1021 97 41 19 126,993 105,458 411 14 90 wt % Ex. 2/10 wt % LDPE 621I 97 37 23 128,593 110,660 319 17 2% 2% Secant Secant Modulus, Modulus, Tear, Tear, Clarity Gloss Haze CD MD CD MD 97 wt % Ex. 2/3 wt % AGILITY 1000 95 34 25 147,512 111,397 277 21 90 wt % Ex. 2/10 wt % AGILITY 1000 97 39 18 131,056 109,028 456 15 90 wt % Ex. 2/10 wt % AGILITY 1001 97 37 22 138,325 106,403 420 16 90 wt % Ex. 2/10 wt % LDPE 751A1 96 36 23 134,211 107,163 381 17 Tensile Tensile Tensile Tensile Tensile Tensile Break Break Yield Break Break Yield Stress, Strain, Stress, Stress, Strain, Stress, CD CD CD MD MD MD Unit psi % Psi psi % psi Ex. 2 4,066 632 4,395 3,941 513 3,996 97 wt % Ex. 2/3 wt % LDPE 640I 3,703 548 4,261 5,550 663 3,897 90 wt % Ex. 2/10 wt % LDPE 640I 3,320 669 4,317 5,182 659 3,716 97 wt % Ex. 2/3 wt % AGILITY 1021 3,456 555 4,458 5,858 677 3,971 90 wt % Ex. 2/10 wt % AGILITY 1021 3,015 552 4,135 4,918 619 3,833 90 wt % Ex. 2/10 wt % LDPE 621I 3,163 555 3,970 4,774 692 3,767 97 wt % Ex. 2/3 wt % AGILITY 1000 4,184 648 4,465 3,383 317 3,894 90 wt % Ex. 2/10 wt % AGILITY 1000 3,354 591 4,217 5,179 643 3,914 90 wt % Ex. 2/10 wt % AGILITY 1001 3,366 606 4,135 5,535 684 3,854 90 wt % Ex. 2/10 wt % LDPE 751A1 3,365 616 3,843 5,323 728 3,717

It is further noted that terms like “preferably,” “generally,” “commonly,” and “typically” are not utilized herein to limit the scope of the claimed invention or to imply that certain features are critical, essential, or even important to the structure or function of the claimed invention. Rather, these terms are merely intended to highlight alternative or additional features that may or may not be utilized in a particular embodiment of the present disclosure.

It will be apparent that modifications and variations are possible without departing from the scope of the disclosure defined in the appended claims. More specifically, although some aspects of the present disclosure are identified herein as preferred or particularly advantageous, it is contemplated that the present disclosure is not necessarily limited to these aspects. 

What is claimed is:
 1. A polyethylene polymer blend having a melt index (I₂)<2 g/10 min, wherein I₂ is measured according to ASTM D1238 at 190° C. and 2.16 kg load, wherein the polyethylene polymer blend comprises: at least about 50% by wt. of at least one high density polyethylene resin (HDPE) having a density ≧0.950 g/cm³, when measured according to ASTM D792; a melt index (I₂)<4 g/10 min; a melt flow ratio (I₁₀/I₂)≦9, where I₁₀ is measured according to ASTM D1238 at 190° C. and 10 kg load; and a molecular weight distribution (MWD) of about 2.0 to about 5, wherein MWD is defined as Mw/Mn with Mw being a weight average molecular weight and Mn being a number average molecular weight; and about 1% to about 20% by wt. of at least one low density polyethylene resin (LDPE) having a density ≦0.930 g/cm³, a melt index (I₂) of about 0.1 to about 10 g/min, and a MWD>3.
 2. The polyethylene polymer blend of claim 1 wherein the polyethylene polymer blend comprises about 2% to about 15% by wt. LDPE.
 3. The polyethylene polymer blend of claim 1 wherein the polyethylene polymer blend comprises about 60% to about 98% by wt. HDPE.
 4. The polyethylene polymer blend of claim 1 wherein the density of the polyethylene polymer blend ≧0.950 g/cm³ and the melt flow ratio (I₁₀/I₂) of the polyethylene polymer blend ≦9.
 5. The polyethylene polymer blend of claim 1 wherein the melt index (I₂) of the polyethylene polymer blend is from about 0.5 to about 1.5 g/10 min.
 6. The polyethylene polymer blend of claim 1 wherein the density of the HDPE is from about 0.955 to about 0.970 g/cm³ and the MWD of the HDPE is from about 2.5 to about
 4. 7. The polyethylene polymer blend of claim 1 wherein the melt index (I₂) of the HDPE is from about 0.5 to about 2 g/10 min and the melt flow ratio (I₁₀/I₂) of the HDPE is from about 6 to about
 8. 8. The polyethylene polymer blend of claim 1 wherein the density of the LDPE is from about 0.915 to about 0.930 g/cm³, and the MWD of the LDPE is from about 4 to about
 10. 9. The polyethylene polymer blend of claim 1 wherein the melt index (I₂) of the LDPE is from about 0.5 to about 7 g/10 min.
 10. An article comprising a polyethylene polymer blend, wherein the polyethylene blend has a melt index (I₂)<2 g/10 min, wherein I₂ is measured according to ASTM D1238 at 190° C. and 2.16 kg load, wherein the polyethylene polymer blend comprises: at least about 50% by wt. of at least one high density polyethylene resin (HDPE) having a density ≧0.950 g/cm³, when measured according to ASTM D792; a melt index (I₂)<4 g/10 min; a melt flow ratio (I₁₀/I₂)≦9, where I₁₀ is measured according to ASTM D1238 at 190° C. and 10 kg load; and a molecular weight distribution (MWD) of about 2.0 to about 5, wherein MWD is defined as Mw/Mn with Mw being a weight average molecular weight and Mn being a number average molecular weight; and about 1% to about 20% by wt. of at least one low density polyethylene resin (LDPE) having a density ≦0.930 g/cm³, a melt index (I₂) of about 0.1 to about 10 g/min, and a MWD>3, and wherein the article has a haze value ≦30% when measured according to ASTM-D-1003.
 11. The article of claim 10 wherein the article has a 2% secant modulus greater than 90,000 psi in the machine direction in accordance with ASTM D882-12.
 12. The article of claim 10 wherein the article has an MD tear of less than 35 g in the machine direction in accordance with ASTM D882-12.
 13. The article of claim 10 wherein the article is a blown monolayer film having a thickness of about 0.5 to about 1.5 mils and the haze value ≦25%.
 14. The article of claim 13 wherein the haze value ≦20%.
 15. The article of claim 10 wherein the polyethylene polymer blend comprises about 2% to about 15% by wt. LDPE, and about 60% to about 98% by wt. HDPE.
 16. The article of claim 10 wherein the density of the polyethylene polymer blend ≧0.950 g/cm³, the melt flow ratio (I₁₀/I₂) of the polyethylene polymer blend ≦9, and the melt index (I₂) is from about 0.5 to about 1.5 g/10 min.
 17. The article of claim 10 wherein the density of the HDPE is from about 0.955 to about 0.970 g/cm³ and the MWD of the HDPE is from about 2.5 to about
 4. 18. The article of claim 10 wherein the melt index (I₂) of the HDPE is from about 0.5 to about 2 g/10 min and the melt flow ratio (I₁₀/I₂) of the HDPE is from about 6 to about
 8. 19. The article of claim 10 wherein the density of the LDPE is from about 0.915 to about 0.930 g/cm³, the MWD of the LDPE is from about 4 to about 10, and the melt index (I₂) of the LDPE is from about 0.5 to about 7 g/10 min. 